Radici Compounds PC10L

聚碳酸酯

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

PC10L is a polycarbonate with a viscosity suitable for general purpose injection molding applications; it is lubricated for ease of mold release. Polycarbonate is an engineering thermoplastic widely recognized for its outstanding toughness, excellent strength, rigidity and creep resistance, electrical insulating characteristics and dimensional stability. Mold shrinkage is low and almost isotropic; this offers benefits in dimensional stability and reduced warpage, and permits the production of complex shape parts to very close dimensional tolerances.

 

Polycarbonate must be dried prior to processing, to fully realize the mechanical properties of the material and the excellent surface appearance typical of parts molded in polycarbonate resins.

 

总体

 

材料状态 • 已商用：当前有效

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

添加剂 • 润滑剂

• 尺寸稳定性良好 • 经润滑 • 收缩性低

性能特点 • 低翘曲性 • 绝缘

• 刚性，高 • 良好的抗蠕变性 • 脱模性能良好

• 高强度 • 韧性良好

用途 • 汽车领域的应用： • 一般目的

外观 • 可用颜色 • 自然色

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.20g/cm³ ASTM D792

收缩率 - 流动 (3.18 mm) 0.50 到 0.70% ASTM D955

吸水率 (24 hr) 0.15% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 2 (屈服, 23°C, 3.18 mm) 63.4MPa ASTM D638

伸长率 2 (断裂, 23°C, 3.18 mm) 100% ASTM D638

弯曲模量 (23°C) 2410MPa ASTM D790

弯曲强度 (23°C) 100MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 850J/m ASTM D256

拉伸冲击强度 3 (23°C) 525kJ/m² ASTM D1822

硬度 额定值单位制 测试方法

洛氏硬度 (R 计秤) 118 ASTM D785

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 130°C ASTM D648

维卡软化温度 154°C ASTM D1525

补充信息

Elongation at Break, ASTM D638, Type I, 73°F, 0.125": 90-110 %

Izod Impact Strength, ASTM D256, Notched, 73°F, 0.125": 15-17 ft-lbs/in

Tensile Impact Strength, ASTM D1822, 73°F, Type "S" specimen: 200-300 ft-lbs/in²

注射 额定值单位制

干燥温度 138°C

干燥时间 2.0hr

建议的最大水分含量 0.020%

螺筒后部温度 282°C

螺筒中部温度 288°C

螺筒前部温度 293°C

加工（熔体）温度 293°C

 

Radici Compounds PC10L

聚碳酸酯

Radici Plastics USA, Inc.

注射 额定值单位制

模具温度 82.2 到 93.3°C

背压 0.345 到 0.689MPa

螺杆转速 40 到 80rpm

 

 

 

 